Active flux for limited pass welding
Good general purpose flux, including semi-automatic
High speed on dirty plate
Good resistance to porosity on rust and primer
Good slag removal, good bead shape
Note: Use another flux for thick plates and multi-pass welding of thick plates (without particular caution) and for low quality steel
Wire grade |
BV |
ABS |
LRS |
DNV |
GL |
cont |
RINA |
RMRS |
CRS |
S-Revix® L12 |
A2TM/ A2YTM/ 2YT |
2YM/ 2YT |
2YM/ 2YT |
2YM/ 2YT |
2YM/ 3YT |
x |
2YT |
|
|
S-Revix® M12К |
A3YT |
|
3YM/ 3YT |
3YM/ 3YT |
3YT |
x |
3YT |
3YT |
3YT |
S-Revis® A2 |
3YT |
|
|
|
|
|
|
|
|
Wire |
C |
Mn |
Si |
P |
S |
Mo |
S-Revix®L12 |
0.07 |
1.4 |
0.6 |
<0.030 |
<0.025 |
|
S-Revix®M12К |
0.07 |
1.6 |
0.7 |
<0.030 |
<0.025 |
|
S-Revis®A2 |
0.07 |
1.6 |
0.6 |
<0.030 |
<0.025 |
0.4 |
FLUX N 203 |
EN 760: S A FB1 54 AC H5 |
||
Flux/wire |
|
||
|
AWS A5.17/A5.23 |
EN 756:MR |
EN 756:TR |
Flux N 203 / S-Revix®L12 |
F7A0-EL12 |
S 42 0 AR/AB S1 |
S 4T 0 AR/AB S1 |
Flux N 203 / S-Revix®M12К |
F7A2-EM12K |
S 42 0 AR/AB S2Si |
S 4T 2 AR/AB S2Si |
Flux N 203 / S-Revis®A2 |
F8A2-EA2-G |
|
S 4T 2 AR/AB S2Mo |
Current type (А) |
DC (+/-)/AC |
Basicity |
0.7 |
Solidification speed |
high |
Density (kg/dm2) |
1,4 |
Grain |
1-20 |
Wire |
Characteristics |
Applications |
S-Revix®L12 |
Lowest cost combination |
Can be used in multipass |
S-Revix®M12К |
Reliable properties |
with low silicon wires |
S-Revis®A2 |
For good impact toughness as welded |
on plates < 25mm with |
|
TR could be selected |
low voltage |
Unit type |
Netto weight (kg) |
Bag |
25 |
«WUTPACK®-SuperBag» |
25 |
Steel drum |
250 |
Big Bag |
1000 |
Wire |
Condition |
Yield Strength 0,2 % (N/mm2) |
Tensile Strength (N/mm2) |
Elongation (%) |
Impact (ISO), J |
|
0 оС |
-20 оС |
|||||
S-Revix®L12 |
MR |
400 |
510 |
28 |
50 |
|
S-Revix®M12К |
TR |
>420 |
>540 |
28 |
|
50 |
S-Revis®A2 |
TR |
>420 |
>550 |
|
|
60 |
MR: multirun, TR: two-run |