Acid melted flux for SA welding. It is developed for welding with speeds over 300 cm/min. Thanks to the applied process of manufacture, grains of flux do not imbibe moisture. In addition, flux alloys metal T-weld with Mn. Flux is intended for butt, angular and lap welds. Flux can be applied for one- and dual-arc welding and equally well works both on Direct and Alternate currents.
Wire grade |
BV |
ABS |
LRS |
DNV |
GL |
CE |
TÜV |
FLUX A 101/Revix® SG2 Ultra |
|
|
|
|
|
X |
X |
FLUX A 101/Revix® SG2 |
|
|
|
|
|
X |
|
FLUX A 101/Revix® Sg3 |
|
|
|
|
|
X |
|
Wire |
C |
Si |
Mn |
Revix®SG2 Ultra |
0.08 |
1.55 |
0.85 |
Revix®SG2 |
0.07 |
1.45 |
0.85 |
Revix®SG3 |
0.07 |
1.65 |
0.90 |
FLUX A 101 |
EN 760: SF MS 1 57 AC |
|
||
Flux/wire |
|
|
||
|
EN/AWS |
EN/AW |
AWS/AW |
AWS/PWHT |
FLUX A 101/Revix® SG2 Ultra |
S1/EL12 |
S 35 2 MS S1 |
A5.17:F6A2-EL12 |
A5.17:F6P2-EL12 |
FLUX A 101/Revix® SG2 |
S2Si/EM12K |
S 38 2 MS S2Si |
A5.17:F7A2-EM12K |
A5.17:F6P2-EM12K |
FLUX A 101/Revix® SG3 |
S2Mo;S Mo/EA2 |
S 42 2 MS S2Mo |
A5.23:F7A2-EA2-A4 |
A5.23:F7P0-EA2-A4 |
Off-shore applications |
Nuclear components application |
High purity weld metal |
Applicable for welding of deep devices |
Current type (А) DC (+/-)/AC
Basicity -0,9
Solidification speed - neutral
Density (kg/cm2)-1,2
Grain-2-20
Bag-25kg
«WUTPACK®-SuperBag »-25 kg
Wire |
Condition |
Yield Strength 0,2 % (N/mm2) |
Tensile Strength (N/mm2) |
Elongation (%) |
Impact (ISO), J |
|
0 |
+20оС |
|||||
Revix®SG2 Ultra |
AW |
490 |
590 |
27 |
110 |
120 |
Revix®SG2 |
AW |
471 |
580 |
25 |
115 |
125 |
Revix®SG3 |
AW |
471 |
595 |
27 |
90 |
110 |
FLUX N 203 |
FLUX N 202 |
FLUX N 201 |
FLUX A 102 |